Surprising spin behavior at room temperature:
circularly polarized room-temperature electroluminescence from spin-polarized light-emitting diodes

Scientists at Tokyo Institute of Technology have observed almost purely circularly polarized electroluminescence from GaAs-based spin-polarized light-emitting diodes at room temperature, with no external magnetic field. This behavior indicates the presence of spin-dependent nonlinear processes, which may allow the development of semiconductor-based spin-photonic devices in the future.

Spin-LED chip placed on a copper block (left) and emitting CP EL (orange spiral arrows); the right- (σ+) and left (σ-)-handed EL components are indicated by the red and blue circles, respectively. QWP, LP, and MCS represent a quarter-wave plate, a linear polarizer, and a multichannel spectrometer, respectively. Inset: EL from a spin-LED chip for different current densities (J).

Figure 1. Spin-LED chip placed on a copper block (left) and emitting CP EL (orange spiral arrows); the right- (σ+) and left (σ-)-handed EL components are indicated by the red and blue circles, respectively. QWP, LP, and MCS represent a quarter-wave plate, a linear polarizer, and a multichannel spectrometer, respectively. Inset: EL from a spin-LED chip for different current densities (J).

The field of spintronics focuses on spin transport behavior in magnetic metals, and the major findings in this area have important implications for the field of electronics. This is because conventional electronics primarily considers the electron charge, whereas spintronics allows the electron spin to be exploited. One of the most significant advancements in spintronics has been the introduction of spin degrees of freedom to semiconductors, which are essential components of modern electronic and photonic applications. However, most experiments investigating spin manipulation in semiconductors have been performed under high magnetic fields and at cryogenic temperatures.

Recently, Specially Appointed Assistant Professor Nozomi Nishizawa and Professor Hiro Munekata and colleagues, from the Institute of Innovative Research, Tokyo Institute of Technology, examined the behavior of spin-polarized light-emitting diodes (LEDs) at room temperature and without an external magnetic field. Hence, they achieved the unexpected result of almost purely circularly polarized (CP) electroluminescence (EL).

The LEDs used in the study contained an epitaxial double heterostructure (sandwich-like structure) of AlGaAs/GaAs/AlGaAs, a crystalline γ-like AlOx tunnel barrier (for electrical stability during operation), and a polycrystalline Fe in-plane spin injector. During operation, spins of a given type were injected into the device. Spin relaxation then caused these spins to disperse and adopt other orthogonal orientations. Radiative recombination subsequently occurred, which was observed in the form of a linearly polarized emission.

Experiments on the LED chips showed that a higher current density generated an increase in the emission intensity. Nishizawa and coworkers also noted that the difference between the left- and right-handed EL components increased with the current density. Specifically, the intensity of the left-handed minority component decreased with increased current density, whereas that of the right-handed majority component increased linearly. Therefore, when the current density was sufficiently high (~100 A/cm2), almost pure CP was achieved. Investigating this behavior in more detail, the researchers found that p-type doping in the active layer allowed the CP observation, which arose from spin-dependent nonlinear processes occurring at a sufficiently high current density.

In the future, higher current densities will be applied in order to elucidate the mechanism behind these nonlinear processes and to investigate the possibility of stimulated CP emission in other geometries. Other important avenues of investigation also exist, e.g., potential spin-LED applications in secure optical communications, cancer diagnosis, and optically enhanced nuclei imaging.

Circularly polarized light

Figure 2. Circularly polarized light
The electric field component of light (yellow bars)
spirally rotates around the propagation axis (z-axis).

Linearly polarized of light

Figure 3. Linearly polarized of light
The electric field componentof the light oscillates
on a given plane.

Reference

Authors: Nozomi Nishizawa1, Kazuhiro Nishibayashi1 and Hiro Munekata1
Title of original paper: Pure Circular Polarization Electroluminescence at Room Temperature with Spin-Polarized Light-Emitting Diodes
Journal: Proceedings of the National Academy of Sciences of the United States of America (PNAS)
DOI : 10.1073/pnas.1609839114outer
Affiliations : 1Institute of Innovative Research, Tokyo Institute of Technology
School of Science

School of Science —Exploring the Truth and Creating Knowledge—
Information on School of Science inaugurated in April 2016

School of Sciencewindow

Schools, Departments, and Institute for Liberal Arts別窓

Further information

Professor Hiro Munekata
Institute of Innovative Research

Email munekata.h.aa@m.titech.ac.jp
Tel +81-45-924-5185

  • RSS

Page Top

CLOSE

CLOSE