Making it crystal clear: Crystallinity reduces resistance in all-solid-state batteries

  • RSS

November 29, 2018

Scientists at Tokyo Tech examined the mechanisms behind the resistance at the electrode-electrolyte interface of all-solid-state batteries. Their findings will aid in the development of much better Li-ion batteries with very fast charge/discharge rates.

Making it crystal clear: Crystallinity reduces resistance in all-solid-state batteries

Designing and improving lithium-ion (Li-ion) batteries is crucial for extending the limits of modern electronic devices and electric vehicles because Li-ion batteries are virtually ubiquitous. Scientists at Tokyo Tech, led by Prof. Taro Hitosugi, had previously reported a new type of all-solid-state battery, also based on lithium ions, which overcame one of the major problems of those batteries: high resistance at the interface between the electrodes and the electrolytes that limits fast charging/discharging.

Although the devices they produced were very promising and were much better than conventional Li-ion batteries in some regards, the mechanism behind the reduced interface resistance was unclear. It has been difficult to analyze the buried interfaces in all-solid-state batteries without damaging their layers. Therefore, Hitosugi and his team of researchers again investigated all-solid-state batteries to shed light on this topic. They suspected that crystallinity (which indicates how well-ordered and periodic a solid is) at the electrode-electrolyte interface played a key role in defining interface resistance.

To prove this, they fabricated two different all-solid-state batteries composed of electrode and electrolyte layers using a pulsed laser deposition technique (Fig. 1 and Fig. 2). One of these batteries had presumably high crystallinity at the electrode-electrolyte interface, whereas the other one did not. Confirming this was possible by using a novel technique called X-ray crystal truncation-rod scattering analysis. "X-rays can reach the buried interfaces without destroying the structures," explains Hitosugi.

Figure 1. Structure of the thin-film all-solid-state batteries

Figure 1. Structure of the thin-film all-solid-state batteries

The batteries were made by stacking thin films of Au (current collector), LiCoO2 (cathode), Li3PO4 (solid electrolyte), and Li (anode) on Al2O3 substrate. (a) Schematic cross-sectional view and (b) microscope photograph of the fabricated thin-film battery.

Figure 2. Conduction path of Li ions at the solid-electrolyte/electrode interface

Figure 2. Conduction path of Li ions at the solid-electrolyte/electrode interface

(a) In the discharge process, Li ions migrate through the solid electrolyte to the interface. Since the LiCoO2 film is (0001)-oriented, the migration of Li ions into LiCoO2 is hindered by the CoO2 layers aligned parallel to the substrate surface. Therefore, Li ions migrate laterally on the surface of LiCoO2, and finally, diffuse into grain boundaries. (b) In the case of the disordered LiCoO2 surface, the diffusion of Li ions along the surface and into the grain boundary is restricted, resulting in a high interface resistance value.

Based on their results, the team concluded that a highly crystalline electrode-electrolyte interface resulted in low interface resistance, yielding a high-performance battery. By analyzing the microscopic structure of the interfaces of their batteries, they proposed a plausible explanation for the increased resistance of batteries with less crystalline interfaces. Lithium ions are stuck at the less crystalline interfaces, hindering ion conductivity. "Controlled fabrication of the electrolyte/electrode interface is crucial to obtain low interface resistance," explains Hitosugi. The development of theories and simulations to further understand the migration of Li ions will be crucial for finally achieving useful and improved batteries for all kinds of devices based on electrochemistry.

This work is carried out in collaboration with Prof. Susumu Shiraki at Nippon Institute of Technology and Senior Researcher Tetsuroh Shirasawa at the National Institute of Advanced Industrial Science and Technology.


Authors : Susumu Shiraki1,2, Tetsuroh Shirasawa3,4, Tohru Suzuki2, Hideyuki Kawasoko2, Ryota Shimizu4,5, and Taro Hitosugi*,2,5
Title of original paper : Atomically Well-Ordered Structure at Solid Electrolyte and Electrode Interface Reduces the Interfacial Resistance
Journal : ACS Applied Materials and Interfaces
DOI : 10.1021/acsami.8b08926 別窓
Affiliations :

1Department of Applied Chemistry, Nippon Institute of Technology

2Advanced Institute for Materials Research (AIMR), Tohoku University

3National Metrology Institute of Japan, National Institute of Advanced Industrial Science and Technology (AIST)


5School of Materials and Chemical Technology, Tokyo Institute of Technology

Further Information

Professor Taro Hitosugi

Department of Chemical Science and Engineering, School of Materials and Chemical Technology

Tokyo Institute of Technology

Tel +81-3-5734-2636


Public Relations Section, Tokyo Institute of Technology

Tel +81-3-5734-2975

  • RSS

Page Top